| 基于SLM的18Ni-300模具钢工艺参数优化 |
| |
| 引用本文： | 朱逸韬、黄卫东.基于SLM的18Ni-300模具钢工艺参数优化[J].福建工程学院学报,2020,0(6):570-575. |
| |
| 作者姓名： | 朱逸韬、黄卫东 |
| |
| 作者单位： | 福建工程学院机械与汽车工程学院快速成型实验室 |
| |
| 摘 要： | 设计了以激光功率、扫描速度、扫描间距、铺粉厚度为因素的正交实验，研究了SLM 成型18Ni-300 模具钢粉末过程中各个工艺参数对成型件致密度的影响规律，并进行了工艺参数优化。实验表明，在选定范围内，成型件致密度随激光功率的增加先增大后减小?随扫描速度的增加持续减小?随扫描间距的增加先增加后减小?随铺粉厚度的增加持续减小。最优工艺参数组为激光功率260 W、扫描速度500 mm/ s、扫描间距0.11 mm、铺粉厚度0.02 mm 时，成型件致密度99.99%，为所有实验中的最优值。
|
| 关 键 词： | 激光选区熔化 致密度 工具钢 田口试验分析 |
Process parameter optimization of 18Ni-300 tool steel based on selective laser melting |
| |
| ZHU Yitao,HUANG Weidong,ZHANG Weijie,CHEN Xiayu,LAI Zhangpeng.Process parameter optimization of 18Ni-300 tool steel based on selective laser melting[J].Journal of Fujian University of Technology,2020,0(6):570-575. |
| |
| Authors: | ZHU Yitao HUANG Weidong ZHANG Weijie CHEN Xiayu LAI Zhangpeng |
| |
| Affiliation: | School of Mechanical and Automotive Engineering, Fujian University of Technology |
| |
| Abstract: | A Taguchi experiment was designed with laser power, scan speed, hatch space and layer thickness as factors. The effects of each processing parameter on the density of the molded parts in the process of SLM of 18Ni-300 tool steel powder was studied, and the process parameters were optimized. Experiments show that in the selected range, the density of the forming part first increases and then decreases with the increase of laser power; with the increase of scanning speed, the density decreases continuously; with the increase of hatch space, it first increases and then decreases; with the increase of layer thickness, it decreases continuously. The optimal process parameters were as follows: when the laser power was 260W, the scanning speed was 500mm/s, the hatch space was 0.11mm, and the layer thickness was 0.02mm, the resulted density was 99.99%, which was the optimal value in all the experiments. |
| |
| Keywords: | selective laser melting (SLM) density tool steel Taguchi experiment |
|