1.
The solubilities of 2-naphthalenesulfonic acid monohydrate and sodium 2-naphthalenesulfonate in sulfuric acid solutions were measured at temperatures ranging from 278.15 to 338.15 K by using a dynamic method. The concentration of sulfuric acid solution ranged from 0 to 80wt%,. The solubilities of 2-naphthalenesulfonic acid monohydrate and sodium 2-naphthalenesulfonate increased with temperature, and both of them were the lowest at 70wt %, of sulfuric acid solution(w~0_3 =0.70)while the highest in pure water. The solubility data were correlated by the modified Apelblat equation. Based on the solubility difference between 2-naphthalenesulfonic acid monohydrate and sodium 2-naphthalenesulfonate, a new technique in which sodium sulfate was used to replace sodium sulfite in the neutralization reaction was developed. The suitable mole ratio of H_2O to Na_2SO_4 in the neutralization reaction was 80∶1, and that of 2-naphthalenesulfonic acid monohydrate to Na_2SO_4 was 3.2∶1. The material balance under the suitable mole ratios was given and discussed.  相似文献   

2.
Al-substituted barium ferrite powders were synthesized using the sol-gel auto-combustion method according to the molecular formula BaAlxFe12-xO19 (x=0, 0.1, 0.2, 0.3, 0.4, 0.5, 1.0). Compared with non-substituted barium ferrite annealing at 1000℃, the vibrating sample magnetometer (VSM) measurement manifested that the optimum magnetic properties formation temperature of Al-substituted barium ferrite was 1100℃. The data from X-ray diffractometer (XRD) showed that with increasing x, the lattice constants (a and c) decreased as well as the unit-cell volume Vcell. Magnetic measurement of non-substituted and Al-substituted powders annealed from 900℃ to 1200℃ exhibited that the maximum magnetization M (10 kOe), the remanent magnetization Mr and the coercivity Hc depended strongly on the chemical composition of powder as well as the annealing temperature. When annealing at 1100℃, BaAl0.5Fe11.5019 of high coercivity Hc (6584 Oe) was produced. Meanwhile, M (10 kOe) and Mr were 42.83emu/g and 25.65emu/g, respectively.  相似文献   

3.
This study deals with the effect of hydrotropes on the solubility and mass transfer coefficient of salicylic acid. The solubility and mass transfer studies were performed using the hydrotropes, i.e., sodium acetate, sodium salicylate, citric acid, and urea at concentrations of 0-3.0 mol/L and system temperatures of 303-333 K. It was found that the solubility and mass transfer coefficient of salicylic acid increases with increase in hydrotrope concentration and also with system temperature. All hydrotropes used in this work showed an enhancement in solubility and mass transfer coefficient to different degrees. The maximum enhancement factor values were determined for all hydrotropes used in this study. The highest value was 28.08 for solubility studies and 10.42 for mass transfer studies. The performance of hydrotropes was measured in terms of the Setschenow constant （Ks）. The highest value observed was 0.696.  相似文献   

4.
Soils can often be contaminated simultaneously by more than one heavy metal. The sorption-desorption behavior of a metal in a soil will be affected by the presence of other metals. Therefore, selective retention and competitive adsorption of the soils to heavy metals can affect their availability and movement through the soils. In this study, the simultaneous competitive adsorption of four heavy metals (Cd, Cu, Hg, and Pb) on ten agricultural soils collected from the Changjiang and Zhujiang deltas, China was assessed. The results showed that the competition affected the behavior of heavy metal cations in such a way that the soils adsorbed less Cd and Hg, and more Pb and Cu with increasing total metal concentrations, regardless of the molar concen- tration applied. As the applied concentrations increased, Pb and Cu adsorption increased, while Cd and Hg adsorption decreased. The adsorption sequence most found was Pb>Cu>Hg>Cd. The maximum adsorption capacity for the heavy metal cations was calculated, and affected markedly by soil properties. The results suggest that Hg and Cd have higher mobility associated to the lower adsorption and that Pb and Cu present the opposite behavior. Significant correlations were found between the maximum adsorption capacity of the metals and pH value and exchangeable acid, suggesting that soil pH and exchangeable acid were key factors controlling the solubility and mobility of the metals in the agricultural soils.  相似文献   

5.
Thirty-six daily time interval PM2.5 samples were collected in different seasonal dates in urban Shanghai, and the concentrations of four anions （Cl- , NO3-, SO4^2-, C2O4^2-） and five cations （NH＋, Na＋, K＋, Ca2＋, Mg2＋） were analyzed with ion chromatography. Sulfate, nitrate and ammonium were found to be the dominant species, accounting for about 80% of the total ions. The daily nitrate to sulfate mass ratio ranged from 0.31 to 0.82, indicating that coal combustion was still the main pollution source in Shanghai. The equivalent ratio of ammonium to stun of nitrate and sulfate showed fixed diurnal variation pattern in all the sampling days with higher values in the nighttime, suggesting that fine particles in the night were more neutralized. The oxalate to sulfate ratio was lower in the winter sampling days than that in hotter summer and autumn sampling days. Oxalate was significantly correlated with sulfate in winter sampling days, but not in the summer and autumn, suggesting that the formation mechanism of oxalate and sulfate was similar in winter, however different in hot days.  相似文献   

6.
Magnetic properties of nanocrystalline Fe60 Cr40 powders prepared by mechanical alloying in vacuum and air were investigated by utilizing the measurements of magnetization, X-ray diffraction, and ^67Fe M（oe）ssbauer spectrum. The results show that the Fe60 Cr40 powders keep the bcc structure during milling in air and vacuum. The saturation magnetization of the Fe60 Cr40 powders milled in vacuum and air decreases with the increase of the milling time up to 45 h. The decrease of saturation magnetization of the Fe60Cr40 powders milled in vacuum is due to the formation of Fe-Cr solid solution, while in air it is due to the formation of paramagnetic disorder structure and solid solution.  相似文献   

7.
Communication technology is changing things. Language is no exception. Some language researchers argue that language is deteriorating due to increased use in electronic communication. The present paper investigated 100 randomly selected electronic mails （e-mails） and 50 short messaging system （SMS） messages of a representative sample of international students in University Putra Malaysia （UPM） to find out the impact of these two specific modes of electronic communication on written language use. The e-mails from UPM International Students Association （UPM-ISA） yahoo group were content analyzed. A non-probability convenience sampling was used to select the 50 short message services sent to the researcher about different subject matters by Malaysian and international students at UPM. Then, they were also content analyzed. The results indicated that the language used in students＇ e-mails and SMS messaging was full of spoken-like spelling, unconventional use of punctuation and abbreviations, and ungrammatical sentences. However, the more in-depth content analysis of the data revealed that the written language is being creatively adapted, developed, and enhanced to suit the conditions of the electronic communication age. Syntactical and lexical reductions are just strategies used to reduce effort, time and space.  相似文献   

8.
In this study, liquid-phase aerobic oxidation of toluene catalyzed by Mn–Mo oxide was conducted in a 1.0 L batch reactor. The macroscopic kinetics of toluene consumption and benzaldehyde generation at 413–443 K were obtained from a combination of experimental observation and hypothetical models. The results clearly showed that both the oxidation rate of toluene and generation rate of the aromatic product were proportional to the concentration of the substrate, the partial pressure of oxygen and the surface area of the catalyst. The energy barrier of toluene oxidation to benzyl alcohol was the highest(≈ 81 kJ mol~(-1)), while that of benzyl alcohol oxidation to benzaldehyde was the lowest(≈ 57 kJ mol~(-1)). Moreover, the activation energy of further oxidation of benzaldehyde in an acetic acid solvent was only slightly lower(≈ 1.9 kJ mol~(-1)) than that of toluene oxidation. Significantly, the transformation of benzyl alcohol indeed contributed to the generation of benzaldehyde and this step conformed to a first-order parallel-consecutive model. Increased reaction temperature and residence time favored the transformation of benzyl alcohol to benzaldehyde. In addition, doping with molybdenum at Mn/Mo = 3/1 enhanced the catalytic performance of the heterogeneous catalyst and was attributed to the presence of a synergetic effect between different metal cations. Regarding the microscopic kinetics, the LH-OS-ND mechanism(Langmuir–Hinshelwood adsorption of reagents on the same type of active sites and non-dissociative adsorption of oxygen) was verified as responsible for the heterogeneous oxidation of toluene. Oxygen and benzaldehyde were weakly adsorbed(Δ H_(ads,Oxy) ≈~(-1)5 kJ mol~(-1), Δ H _(ads)0,Bald) ≈-30 kJ mol~(-1)), but showed strong mobility(Δ S_(ads,Oxy) ≈-22 J mol~(-1) K~(-1)), Δ S_(ads,Bald) ≈-39 J mol~(-1) K~(-1)). The fundamental intrinsic rates were deduced based on the LH-OS-ND mechanism and showed great consistency with the macroscopic results.  相似文献   

9.
The effects of particle size of activated carbon （AC） on its wettability, electrode coating technology and electric chemical performance were studied to assemble nonaqueous electric double layer capacitors （EDLCs） for high power requirements. The results show that the specific surface area and total pore volume of AC decrease from 2 137 m^2/g to 1 683 m^2/g, and 0.95 cm^3/g to 0.78 cm^3/g, respectively, if it is ball-milled for 8 h. The pore size distributions are similar in the range of 0.7 nm to 3.5 nm for different ball-milling time. There exists oxidation on the surface of AC during the ball-milling process and the ratios of O-C=O oxygen compositions increase whereas those of C-O, C=O decrease. The peeling strength of AC coated on current collector is almost inverse proportion with the particle size of AC as well as the resistance of EDLCs, and its capacitance decreases about 6%.  相似文献   

10.
A new series of Schiff base ligands were synthesized by the condensation of 2-amino-5-mercaptan-l,3,4-thiadiazole and salicylaldehyde or 2,4-dihydroxybenzaldehyde and their derivatives with choroacetic acid, and further reaction with corresponding metal acetate to form metal complexes. The compositions and structures of the ligands and their complexes were characterized by elemental analysis, molar conductivities, electronic absorption spectra and infra-red spectra. Their inhibition rates to free radical, such as O2, were also tested. The results show that all of the obtained complexes display significant activities, among which the copper（Ⅱ） complexes have the best inhibitive effects.  相似文献   

11.
Exchange coupling and magnetization reversal mechanism in two series of Co_xNi_(1-x)/CoO(30 nm)(x=0.2 and 0.4)bilayers are studied by vector magnetometer.Two components of magnetization are measured parallel and perpendicular to the applied field.At low temperatures,coercivity H_c∝(t_(FM))~(-n),n=1.5 and 1.38 for x=0.2 and 0.4,respectively,in agreement with the random field model.At room temperature,the coercivity is nearly proportional to the inverse FM layer thickness.In addition to the exchange field and the coercivity,the characteristic of the magnetization reversal mechanism was found to change with temperature.At temperatures below 180 K,magnetization reversal process along the unidirectional axis is accompanied only by nucleation and pinning of domain wall while magnetization rotation is also involved at high temperatures.  相似文献   

12.
The amorphous Fe67.5 alloy particles have been prepared by mechanical alloying(MA) process of elemental powders.The crystallization is observed at temperature around 405℃ by means of differential thermal analyzer,It is found that the coercivity Hc and the effective magnetic anisotropy value of amorphous phase are not far from that of crystal phase.The magnetization behavior of amorphous and nanocrystalline samples prepared by mechanical alloying and milling process are quite similar,they obey 1/H law at middle-high field and 1/H^2 at higher field.The 1/H field dependence is attributed to a large number of dislocations created during MA process.The studies on the 1/H^2 field dependence reveals that magnetization of Fe-Ni ultrafine particles are governed predominantly by internal stress fields induced by MA process.  相似文献   

13.
This work investigated the microwave dielectric properties of A-site substitution by rare earth La3+in(Pb0.5Ca0.5)(Fe0.5Ta0.5)O3(PCFT) system.A single perovskite phase was obtained only when the doping content was 2%.Suitable La3+ doping improved microwave dielectric performances.Excessive La3+doping caused the formation of secondary phase,which resulted in the decreasing of permittivity εrand quality factor Qfvalues.Especially,when the doping content is 2%-5%,permittivity εrwas above 75 and Qfvalues were 6...  相似文献   

14.
The synthesis of methanol and dimethyl ether (DME) from CO hydrogenation has been investigated on Cu-based catalysts. A series of Cu/ZnO/Al2O3 catalysts were prepared using a solvent-free routine which involved a direct blend of copper/zinc/aluminum salts and citric acid, followed by calcination at 450 °C. The calcination processes were monitored using thermogravimetry differential scanning calorimetry (TG-DSC). Catalysts were further characterized using N2 adsorption, scanning electronic microscopy (SEM), X-ray diffraction (XRD), N2O oxidation followed by H2 titration, and temperature-programmed reduction with H2 (H2-TPR). The reduction processes were also monitored with in-situ XRD. The physicochemical properties of catalysts depended strongly on the types of precursor salts, and catalysts prepared using Al acetate and Cu nitrate as starting materials had a larger surface area, larger exposed metallic copper surface area, and lower reduction temperature. The CO hydrogenation performances of these catalysts were compared and discussed in terms of their structures. Catalysts prepared with copper nitrate, zinc and aluminum acetates exhibited the highest catalytic activity.  相似文献   

15.
以木屑为原料,高温热解制备生物炭。以聚乙烯醇为粘结剂,采用混合法将生物炭与果胶复合,并负载磁性,经烘干定型制备果胶包覆的磁性生物炭材料（果胶@生物炭-Fe3O4）。采用扫描电镜（SEM）、X射线衍射（XRD）及N2吸附-脱附（BET）等方法对果胶@生物炭-Fe3O4进行表征,结合吸附实验分析其对Cu2+的吸附特性。结果表明,当生物炭、果胶、Fe3O4质量比为5：1：1,溶液pH值为6,吸附24 h,果胶@生物炭-Fe3O4对Cu2+吸附效果最好;二级动力学方程能较好地描述果胶@生物炭-Fe3O4对Cu2+的吸附过程,Freundlich模型能较好地拟合其吸附行为;SEM结果显示该材料具有不规则的孔隙结构;XRD分析显示纳米Fe3O4是其主要的晶体结构;BET测得其比表面积为25.654 m2·g-1,平均孔径为20.18 nm。  相似文献   

16.
1　Introduction　Ahugeamountofliteratureexistsonthestudyofi dentifyingtracemetalionsbymeansofspectropho tometry[1 3] ,fluorimetry[4 6 ] aswellas polarogra phy[7 9] ,whichhaveactiononlocatingtheendpointoftheindicatingreaction .Howeverbothspectropho tometryandfluorimetryareeasytobeinterferedbycolororprecipitation ,whilepolarographyhasanissueofmercurypollution .Thecatalyzingkineticanalysishasthecharacteristicsofhighsensitivityandspeedi ness.Oscillographicpotentiometryisasimpleintu itionisticanal…  相似文献   

17.
SO4^2- / TiO2-La2O3, a novel solid superacid, was prepared and its catalytic activities at different synthetic conditions are discussed with esterification of n-butanoic acid and n-butyl alcohol as probing reaction. The optimum conditions have also been found, mole ratio of n（La^3＋）：n（Ti^4＋） is 1：34, the soaked consistency of H2SO4 is 0.8 tool/L, the soaked time of HESO4 is 24 h, the calcining temperature is 480 ℃, the calcining time is 3 h. Then it was applied in the catalytic synthesis often important ketals and acetals as catalyst and revealed high catalytic activity. Under these conditions on which the molar ratio of aldehyde/ketone to glycol is l： 1.5, the mass ratio of the catalyst used in the reactants is 0.5%, and the reaction time is 1.0 h, the yields of ketals and acetals can reach 41.4%-95.8%.  相似文献   

18.
(K0.47Na0.47Li0.06)NbO3 (KNLN) lead-free ceramics were prepared by molten salt synthesis (MSS) method using k2CO3-Na2CO3 eutectic mixtures as the flux. The microstructure and piezoelectric properties when sintered at 980-1 030 ℃ were investigated. The calcined powders were examined by X-ray diffraction. The microstructure of the calcined powders and sintered bodies was observed using a scanning electron microscope (SEM).The piezoelectric constant d33 was measured using a quasi-static piezoelectric d33 meter. The planar coupling coefficient Kp was calculated by resonance-antiresonance method. The experimental data for each sample's performance indicators were the average values of 8 specimens. The relative densities of sintered specimens are above 97%, and the dielectric loss is below 0.03. It was found that (K0.47Na0.47Li0.06)NbO3 prepared by MSS is compact and lead-free. The piezoelectric constant d33 is 216 pC·N-1 and the planar electromechanical coupling factor Kp is 0.352.  相似文献   

19.
Fluorescence properties of Eu^3 :Y2SiO5 have been investigated.Transitions between ^5D and ^7Fwere were studied with transmission spectra,fluorescence spectra,photoluminescence excitation(or absorption) spectra and site selective fluorescence spectra.The X-ray powder diffraction pattern of Eu^3 :Y2SiO5 shows that the crystal belong to monoclinic,and lattice‘s constants a,b,c and β arc obtaned by a simulation with the measured diffraction angles.  相似文献   