Change and control of nitrogen in molten steel production process |
| |
| Authors: | XIONG Shuang ZENG Hui CAO Yang and WANG Qing-xiang |
| |
| Institution: | Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, P. R. China;Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, P. R. China;Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, P. R. China;Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, P. R. China |
| |
| Abstract: | The change and control of nitrogen content in molten steel was investigated through the production process of "LDBAr-LF-RH-CC". Results show that nitrogen content reduces gradually in converter-steelmaking stage, rises rapidly from the end of converter process to the end of argon station process, continues to increase in ladle furnace process, and decreases slightly in RH refining stage. Since nitrogen is removed mainly by BOF steelmaking and vacuum refining operations, nitrogen in molten steel should be removed as much as possible in these two operations. However, nitrogen uptake should be minimized in other operations of molten steel production process. |
| |
| Keywords: | molten steel production process nitrogen content change control |
| 本文献已被 CNKI 维普 等数据库收录！ |
| 点击此处可从《重庆大学学报(英文版)》浏览原始摘要信息 |
| 点击此处可从《重庆大学学报(英文版)》下载免费的PDF全文 |
|