Effects of silica nanoparticle and GPTMS addition on TEOS-based stone consolidants |
| |
| Institution: | 1. Physics Department, National Technical University of Athens, Zografou Campus, 15780 Athens, Greece;2. Centro de Biomateriales e Ingeniería Tisular, Universitat Politècnica de València, Camino de Vera s/n, 46022 Valencia, Spain;3. 3B''s Research Group—Biomaterials, Biodegradables and Biomimetics, University of Minho, Headquarters of the European Institute of Excellence on Tissue Engineering and Regenerative Medicine, AvePark, 4806-909, Taipas, Guimarães, Portugal;4. ICVS/3B''s, PT Government Associate Laboratory, Braga, Guimarães, Portugal;5. Ciber en Bioingeniería, Biomateriales y Nanomedicina (CIBER-BBN), Spain |
| |
| Abstract: | Consolidants based on tetraethoxysilane (TEOS) have been widely used for the consolidation of decaying stone heritages. These products polymerize within the porous structure of the decaying stone, significantly increasing the cohesion of the material. However, TEOS-based consolidants suffer from practical drawbacks, such as crack formation of the gel during the drying phase due to the developed capillary force, which is typical for TEOS-based consolidants. We have prepared new consolidants TEOS-based consolidants containing flexible (3-glycidoxypropyl) trimethoxysilane (GPTMS) and silica nanoparticles in order to reduce capillary force development during gel drying, and have characterized them for the application of stone consolidants. Different sizes of silica nanoparticles were used, which were smaller than the pore size of the tested stone. The properties of the TEOS/GPTMS/nanoparticle composite solution were compared with those of the commercial products Wacker OH and Unil sandsteinfestiger OH 1:1. The gelation time was similar to that of commercial consolidants, and the TEOS/GPTMS/nanoparticle solution was stable over a period of up to six months. The contact angle of the surface increased with the addition of the nanoparticle, as well as with the addition the GPTMS, which is higher than that of commercial Wacker OH. The addition of a nanoparticle, as well as GPTMS having flexible segment, provided a crack-free material, while the gels obtained from the commercial consolidants exhibited cracking. |
| |
| Keywords: | |
| 本文献已被 ScienceDirect 等数据库收录！ |
|