Microstructure and mechanical properties analysis of β-tricalcium phosphate/carbon nanotubes scaffold based on rapid prototyping |
| |
引用本文: | 林柳兰,申营营,张加峰,方明伦.Microstructure and mechanical properties analysis of β-tricalcium phosphate/carbon nanotubes scaffold based on rapid prototyping[J].上海大学学报(英文版),2009,13(5):349-351. |
| |
作者姓名: | 林柳兰 申营营 张加峰 方明伦 |
| |
作者单位: | Key Laboratory of Machinery Automation and Robotics, Shanghai University, Shanghai 200444, P. R. China |
| |
基金项目: | the Innovation Program of Shanghai Municipal Education Commission (Grant No.09YZ34) |
| |
摘 要: | β-TCP ceramic scaffolds were fabricated with selective laser sintering(SLS)in this work. Carbon nanotubes(CNTs)were mixed with porous β-TCP matrix to enhance the mechanical performance of the bone tissue engineering scaffolds. Scaffold reconstruction and microstructure analysis were fulfilled based on micro-computed tomography(Micro-CT)scanning data.Results show that the strength of scaffold mixed with 0.2% CNTs reaches 0.819 MPa which has been improved by 85.7% compared with that without CNTs. Micro-CT analysis shows that the scaffold has a good interconnectivity, and pore size mainly distributes in the two regions of 60-340 μm and 500 620 μm.
|
关 键 词: | β-tricalcium phosphate scaffold |
收稿时间: | 2009-01-08 |
修稿时间: | 2009-05-16 |
本文献已被 CNKI 维普 万方数据 SpringerLink 等数据库收录! |
| 点击此处可从《上海大学学报(英文版)》浏览原始摘要信息 |
| 点击此处可从《上海大学学报(英文版)》下载免费的PDF全文 |