Tribology Performance and Adhesive Strength Evaluation of TiAlSiN Coating |
| |
| Authors: | JIANG Feng XIE Hong RONG Yiming YAN Lan |
| |
| Institution: | JIANG Feng 1,XIE Hong 2,3,RONG Yiming 1,YAN Lan 1 (1. State Key Laboratory of Tribology,Department of Precision Instruments and Mechanology,Tsinghua University,Beijing 100084,China,2. Machine Tool Factory,Dongfang Turbine Co,Ltd,Deyang 618000,3. College of Materials Science and Engineering,Sichuan University,Chengdu 610064,China) |
| |
| Abstract: | Scratch test and friction test were performed to evaluate the internal and external interface behaviors of TiAlSiN coating, respectively. The critical compressive and shearing stress of coating failure during scratch test were calculated and the values are 30.84 MPa and 4.98 MPa respectively. The average friction coefficients of TiAlSiN coating against 2Cr12Ni4Mo3VNbN steel are 0.70 (sliding speed 50 m/min), 0.63 (sliding speed 100 m/min), and 0.81 (sliding speed 150 m/min). The elements diffusion was analy... |
| |
| Keywords: | TiAlSiN coating internal and external interface scratch test ball-on-disc friction test |
| 本文献已被 CNKI 维普 SpringerLink 等数据库收录！ |
|