1.
In this study, supported nonmetal （boron） doping TiO2 coating photocatalysts were prepared by chemical vapor deposition （CVD） to enhance the activity under visible light irradiation and avoid the recovering of TiO2. Boron atoms were successfully doped into the lattice of TiO2 through CVD, as evidenced from XPS analysis. B-doped TiO2 coating catalysts showed drastic and strong absorption in the visible light range with a red shift in the band gap transition. This novel B-TiO2 coating photocatalyst showed higher photocatalytic activity in methyl orange degradation under visible light irradiation than that of the pure TiO2 photocatalyst. 相似文献
2.
An efficient visible-light-responsive BiOBr/TiO2 heterojunction nanocomposite was fabricated successfully using in-situ depositing technique at room temperature by introducing BiOBr onto the surface of TiO2 nanobelts pre-prepared by hydrothermal reaction and etched with H2SO4. The obtained particles were characterized by XRD, SEM, TEM, XPS, UV-Vis DRS and PL techniques. BiOBr/TiO2 heterojunction nanocomposites with different mass ratios of m(BiOBr)/m(TiO2) were discussed in order to get the best photocatalytic activity, and BiOBr/TiO2-1.0 was proved to be the optimal mass ratio. BiOBr/TiO2-1.0 exhibited excellent photocatalytic activity in the degradation of RhB compared with TiO2 nanobelts, pure BiOBr and the mechanical mixture of TiO2 nanobelts and BiOBr. At last, a possible mechanism of photocatalytic enhancement was proposed. 相似文献
3.
A Pr-doped TiO2-NTs/SnO2-Sb electrode was prepared by a simple method, cyclic voltammetry(CV). The methyl orange(MO)aqueous solution was selected as a simulated wastewater. The ordered microstructural TiO2-NTs substrate was synthesized by an electrochemical method to obtain large specific surface area and high space utilization. The phase structure, electrode surface morphology and electrochemical properties of electrodes were characterized by XRD, SEM and electrochemical technology, respectively. The results showed that praseodymium oxide was successfully doped into the SnO2-Sb film by CV method. Due to the doped Pr, the oxygen evolution potential increased from 2.25 V to 2.40 V. The degradation of MO was investigated by UV-vis. The C t /C 0 (φ) was studied as a function to obtain the optimal parameters, such as the amount of doped Pr, current density and initial dye concentration. In addition, the degradation process followed pseudo-first-order reaction kinetics and the rate constant was 0.099 3 min-1. The result indicated that the introduction of Pr reduced the formation of oxygen vacancies or enhanced the formation of adsorbed hydroxyl radical groups on the surface, thus leading to better activity and stability. 相似文献
4.
TiO2 nanoparticles(NPs)were prepared via the hydrothermal route of TiO2 xerogel in nitric acid, hydrochloric acid and acetic acid. The physico-chemical properties of the powders were characterized by X-ray diffraction(XRD)and N2 adsorption desorption techniques. The effects of the different acids on the structure(crystal phase)and texture(primary particle size and porosity)of the TiO2 powders were explored. Results indicated that acetic acid facilitated the formation and stability of pure anatase phase. On the other hand, nitric acid and hydrochloric acid led to the transformation from anatase to rutile. The catalyst synthesized via the hydrothermal route of TiO2 xerogel in the low concentration hydrochloric acid solution(Ti-HCl-0.15)had the highest photocatalytic activity than the catalysts obtained in the other two acid solutions. The effects of the different acids were discussed in terms of acid strength, chelating effect and the thermal stability of the adsorbed acidic anions. 相似文献
5.
Ba0.6Sr0.4TiO3 （BST） thin films with and without HfO 2 buffer layer were fabricated on Pt/Ti/SiO2/Si substrates by pulsed laser deposition. Dependences of HfO 2 thickness on the dielectric property and leakage current of BST thin films were focused. The dielectric constant of BST thin films increased and then decreased with the increase of HfO 2 thickness, while the dielectric relaxation was gradually improved. The loss tangent and leakage current under positive bias decreased with the HfO 2 thickness increasing. The leakage current analysis based on the Schottky emission indicated an improvement of the BST/Pt interface with HfO 2 buffer layer. The loss tangent, tunability and figure of merit of optimized HfO 2 buffered BST thin film achieved 0.009 8, 21.91% （E max = 200 kV/cm）, 22.40 at 10 6 Hz, respectively. 相似文献
6.
Silicon carbide (SiC) composites were prepared by hot-press sintering from α-SiC starting powders with BaAl2Si2O8 (BAS). The effects of additives on densification, microstructure, flexural strength, and fracture behavior of the liquid phase sintered (LPS) SiC composites were investigated. The results show that the served BAS effectively promotes the densification of SiC composites. The flexural strength and fracture toughness of the SiC composites can reach a maximum value of 454 MPa and 5.1 MPa·m1/2, respectively, for 40% (w/w) BAS/SiC composites. SiC grain pullout, crack deflection, and crack bridging were main toughening mechanisms for the sintered composites. 相似文献
7.
A new supported amorphous catalyst CoP/TiO2 was prepared by chemical reduction and characterized by ICP, XRD, TEM, BET and DSC Its application in decomposing PH3 to high purity phosphor and its catalytic activity were studied. The decomposition rate is over 95% at 450 ℃. For comparison, unsupported CoP amorphous catalyst was prepared by the same method. The result suggests that CoP/TiO2 exhibits higher thermal stability and catalytic activity than CoP, which is attributed to the high dispersion of CoP alloy particles on the support-TiO2. 相似文献
8.
A skutterudite-related antimonide, CoFe3Sb12, was prepared with vacuum melting. XRD analysis showed the material contained Sb, FeSb2, CoSb2 and CoSb3 phases. The electrochemical properties of the ball-milled CoFe3Sb12−10 wt% graphite composite were studied using pure lithium as the reference electrode. A maximal lithium inserting capacity
of about 860 mAh/g was obtained in the first cycle. The reversible capacity of the material was about 560 mAh/g in the first
cycle and decreased toca. 320 mAh/g and 250 mAh/g after 10 and 20 cycles respectively.Ex-situ XRD analyses showed that the antimonides in the pristine material were decomposed after the first discharge and that antimony
was the active element for lithium to insert into the host material.
Project supported by the National Natural Foundation of China (No. 59771032) and the RFDP of the Education Ministry of China
(No. 20010335045) 相似文献
9.
TiO2/ ormosil planar waveguide was prepared by sol-gel method at low thermal treatment temperature （ 〈 200 ℃）. Scanning electron microscope, FT-IR spectrometer, spectrophotometer, atomic force microscopy, thermal analyzer, and dark m-line spectroscopy were used with the method of scattering-detection to investigate optical and structural properties. High optical quality waveguide film was obtained. The propagation loss of film was 0.569 dB/cm at a wavelength of 632.8 nm. 相似文献
10.
In2O3 Ultrafine Powder Synthesis by Sol—Gel Method 总被引：1，自引：0，他引：1
The precursor of ultrafine In2O3 powder was prepared by the hydrolysis,peptization and gelation of InCl3.4H2O used as raw material.After calcination,ultrafine In2O3 powder was obtained.The particles were characterized by the methods of thermo-gravimetric and differential thermal analysis(TG-DTA),X-ray diffractometry(XRD) and transmission electron microscopy(TEM).respectively. 相似文献
11.
In the present work,hierarchical nanostructured titanium dioxide（TiO2） films were fabricated on Ti-25Nb-3Mo-2Sn-3Zr（TLM） alloy for biomedical applications via one-step anodization process in ethylene glycolbased electrolyte containing 0.5wt% NH4F.The nanostructured TiO2 films exhibited three distinct types depending on the anodization time：top irregular nanopores（INP）/beneath regular nanopores（RNP）,top INP/middle regular nanotubes（RNT）/bottom RNP and top RNT with underlying RNP.The evolution of the nanostructured TiO2 films with anodization time demonstrated that self-organizing nanopores formed at the very beginning and individual nanotubes originated from underlying nanopore dissolution.Furthermore,a modified two-stage self-organizing mechanism was introduced to illustrate the growth of the nanostructured TiO2 films.Compared with TLM titanium alloy matrix,the TiO2 films with special nano-structure hold better hydrophilicity and higher specific surface area,which lays the foundation for their biomedical applications. 相似文献
12.
The photocatalytic activity of the mixtures of TiO2 with the rare earth oxide La was investigated. The study on the effect of the rare earth oxide content, calcinating temperature
and calcinating time on the performance of the mixture revealed that sample treated under higher temperature and longer time
had higher photoactivity than pure TiO2. The experimental results of polycrystalline X-ray diffraction showed that the extent of the lattice expansion varied with
the variation of calcinating temperature of time. It is suggested that this might be due to the variation of La content diffused
into the TiO2 lattice. The La in the lattice may inhibit the recombination of photogenerated electron-hole pairs and thus enhance the photoactivity. 相似文献
13.
TiO2 fibers were prepared via alternatively introducing water vapor and Ti precursor carried by N2 to an APCVD （chemical vapor deposition under atmospheric pressure） reactor at ≤200 ℃. Activated carbon fibers （ACFs） were used as templates for deposition and later removed by calcinations. The obtained catalysts were characterized by scanning electron micros- copy （SEM）, transmission electron microscopy （TEM）, Brunauer, Emmett and Teller （BET） and X-ray diffraction （XRD） analysis The pores within TiO2 fibers included micro-range and meso-range, e.g., 7 nm, and the specific surface areas for TiO2 fibers were 141 m^2/g and 148 m^2/g for samples deposited at 100 ℃ and 200℃ （using ACFI700 as template）, respectively. The deposition temperature significantly influenced TiO2 morphology. The special advantages of this technique for preparing porous nano-material include no consumption of organic solvent in the process and easy control of deposition conditions and speeds. 相似文献
14.
Glass-ceramics obtained from the electric arc furnace molten slag of incinerator fly ash was produced by applying nucleation and crystallization through heat treatment process. The effects of nucleating agent (TiO2 and Cr2O3)on the crystallization kinetics and heat treatment schedule of the slag were investigated. The results show that the nucleating agents changed the crystallization phase and morphology of the obtained glass-ceramics. The optimum heat treatment schedule of the glass with TiO2 was determined as nucleation at 952 K for 1.5 h and crystal growth at 1258 K for 1.5 h, while those values with Cr2O3 were estimated at 971 K for 2 h and at 1 238 K for 2 h. TiO2 acting as nucleating agent could decrease the activation energy of the slag and shorten the total thermal treatment time in comparison with Cr2O3. The glass-ceramics obtained under the optimum heat treatment condition was environment-friendly and had remarkable physical/mechanical properties and chemical durability. 相似文献
15.
The influence of calcination temperature on TiO2 nanotubes＇ catalysis for TiO2/UV/03 was investigated. TiO2 nanotubes （TNTs） were prepared via the sol-gel method and calcined at 300--700 ℃, which were labeled as TNTs-300, TNTs-400, TNTs-500, TNTs-600 and TNTs-700, respectively. TNTs were characterized by transmission electron microscopy （TEM） and X-ray diffraction （XRD）. It is found that TNTs calcined at 400 ℃ showed the best thermal stability. When the calcination temperature increased from 400 ℃ to 700 ℃, the special structure of tubes was destroyed and gradually converted into nanorods and/or particles. The transformation from anatase to rutile occurred at 600 ℃, and the rutile phase was enhanced when the calcination temperature was increased to over 600 ℃. The calcina- tion temperature＇s influence on TNTs＇ adsorption activity for for TiO2/UV/O3 was investigated in landfill leachate solution chemical oxygen demand （COD） and catalytic activity In landfill leachate solution, the adsorption activity of COD decreased in the reduced order of TNTs-300, TNTs-400, TNTs-500, TNTs-600 and TNTs-700. In photocatalytic ozonation, TNTs-400 showed the best catalytic activity while TNTs-700 exhibited the worst. In other three processes, the COD removal of TNTs-300/UV/O3 was higher than those of TNTs-500/UV/O3 and TNTs-600/UV/O3 in the first 20 rain, and then became close to those of the latter two in the following 40 rain. Compared with TNTs-300 and TNTs- 400, TNTs-600 had the best anti-fouling activity, while TNTs-500 and TNTs-700 had lower anti-fouling activity than the former three. In photocatalytic ozonation, the calcination temperature of 400 ℃ was appropriate when TNTs were obtained at the synthesis temperature of 105 ℃. 相似文献
16.
Internal exposure of university students to polycyclic aromatic hydrocarbons(PAHs)was assessed through urinary PAHs metabolites. Eight monohydroxylated PAHs(OH-PAHs)were detected with high performance liquid chromatography (HPLC). The detectable frequencies were 59%-100% for different analytes. Major components in the subjects‘ urine were 2-hydroxynaphthalene(2-OHNap, 0.60 μg/mmol creatinine), followed by hydroxyphenanthrene(ΣOH-Phe, 0.38 μg/mmol cre-atinine)and 2-hydroxyfluorene(2-OHFlu, 0.25 μg/mmol creatinine). Excretion of 1-hydroxypyrene(1-OHPyr, 0.08 μg/mmol creatinine)was almost one order of magnitude lower than the 2-OHNap level in the urine samples. Phenanthrene can be metabolized to five monohydroxy metabolites in human urine. In the present study, 1-or 9-hydroxyphenanthrene(1-or9-OHPhe)was the dominant component(79%), followed by 2-+3-OHPhe(18%)and 4-OHPhe(3%). The study indicates that 1-OHPyr may not be a good marker for total PAHs exposure, and monitoring of 2-OHNap, 2-OHFlu, 1-or 9-OHPhe and 1-OHPyr as multiple biomarkers are more suitable than only using 1-OHPyr. The levels of OH-PAHs detected in urines of students living in Shanghai are higher those of people in other countries or regions. The concentrations of urine OH-PAHs are directly related to the exposure to PAHs in the environment, indicating that Shanghai residents are at high health risk. 相似文献
17.
Well-cubic perovskite lanthanum aluminate (LaAlO3) film on (110) silicon substrate was fabricated by sol-gel method with corresponding inorganic salts. Lanthanum acetate and
aluminum acetate glacial acetic acid solutions were prepared via ligand exchange starting from lanthanum nitrate hexahydrate
and aluminum nitrate hexahydrate after being refluxed. (CH3CO)2O removed nitrates and the crystallized H2O completely, acetylacetone (AcAc) was partially bidentated with metallic ion of the metallic acetates and formed La(OAc)3−x
(AcAc)
x
which were hydrolyzed into La(AcAc)3−x(OH)
x
by adding 10 ml 0.4% methyl cellulose (MCL) solution. The La(AcAc)3−x
(OH)
x
, polymerizing and combining with MCL, formed the LaAlO3 sol precursor with heteropolymeric structure and formed film easily. The epitaxial LaAlO3 film on Si(110) substrate was crystallized after being annealed in thermal annealing furnace for 650–750 °C/30 min. The morphologies
and microstructures were characterized. The refractive index of the LAO film was 1.942 to 2.007; the dielectric constant and
the dissipation factors were estimated to be 23–26 and 2.1×10−4−2.4×10−4 respectively.
Project (No. 2002CB613305) supported by the National Basic Research Program (973) of China 相似文献
18.
Titanium silicalite (TS-1) without and with extra-framework titanium have been prepared and TiO_2 is also prepared under the same conditions.All the samples are characterized with XRD,FT-IR,and UV–Vis.The effects of extra-framework titanium in TS-1 on the ammoximation of cyclohexanone have been studied in a continuous slurry reactor.The characterization results reveal that the extra-framework titanium exists as anatase.The catalytic evaluation results show that the anatase has a positive effect on the ammoximation of cyclohexanone by extending the catalytic life because it also exhibits some activity,while the conversion of cyclohexanone and the selectivity to cyclohexanone oxime are not influenced.The anatase TiO_2 does not catalyze H_2O_2 decomposition appreciably compared with TS-1 without extra-framework titanium.The results are very useful in guiding the TS-1 production. 相似文献
19.
Xian-jin Yu Ph. D. Guang-li Zhang Zhu-xian Qiu Min-shou Zhao Qiang Su 《上海大学学报(英文版)》1999,3(3):251-254
ZnFe2O4 and ZnFe2O4-based materials were tested to obtain the electrical conductivity and corrosion resistance in melting bath for aluminum electrolysis.
The results proved that adequate additives, such as Ni2O3 CuO, Cu, ZnO and CeO2 would increase the electrical conductivity, and the ZnFe2O4-based anodes with these additives were of good corrosion resistance. The current density on anode, the mole ratio of NaF/AlF3 (MR) and the content of alumina in the bath effect the anode corrosion rate in different way.
Project supported by the Science Foundation of Liaoning Province, P. R. China (95 – 156) 相似文献
20.
The chemisorption properties of N18O adsorption on TiO2(110) surface were investigated by experimental and theoretical methods. The results of temperature programmed desorption
(TPD) indicated that the temperatures of the three desorption peaks of the main N2 molecules were at (low) temperature of 230 K, 450 K and (high) temperature of 980 K. This meant that N18O decomposed and recombined during the process of N2 desorption after N18O was exposed. Analysis of the stable combination and orbital theory calculation of the surface reaction of NO adsorption
on the TiO2(110) cluster model showed that there was clear preference for the Ti-NO orientation. 相似文献