冻融是混凝土结构随季节变化所必须经历的阶段,随着冻融次数的增加,混凝土的表观特征和强度将发生退变.采用冻融次数为0、30、50、70、100次,对补偿收缩混凝土进行冻融循环试验,分析补偿收缩混凝土的表面特征和强度劣化趋势,发现随着冻融次数的增加,普通混凝土与补偿收缩混凝土相比,表面破坏更严重,混凝土抗压和抗折强度呈现下降趋势.冻融100次后,普通混凝土抗压、抗折强度分别下降35.2%和44.1%,而补偿收缩混凝土抗压、抗折强度分别下降30.3%和35.3%,说明适当掺入膨胀剂对提高混凝土的抗冻性有一定的作用,有利于控制和降低混凝土冻融环境下强度的退化. 相似文献
4.
To investigate the effects of salt concentration and freeze-thaw （FT） on the first hydration shell of Zn2+ ions in Zn（NO3）2 aqueous solutions, extended X-ray absorption fine structure （EXAFS） spectroscopy was used to examine Zn K-edge EXAFS spectra of Zn（NO3）2 aqueous solutions with various concentrations before and after FT treatment. The influences of salt concentration and freeze-thaw on the structural parameters of the first hydration shell of Zn2+ ions, including hydration number, Zn-O distance and thermal disorder, were analyzed. The results show that Zn2+ ions have 3.2―6.8 nearest oxygen neighbors with the Zn-O distance being 0.202―0.207 nm. In highly concen-trated solutions, Zn2+ ions are hydrated with four water molecules in a tetrahedral form. The dilution of Zn（NO3）2 aqueous solutions increases the number of water molecules in the first hydration shell of Zn2+ ions to six with their octahedral arrangement. Both the hydration number in the first hydration shell of Zn2+ ions and the degree of thermal disorder increase when the FT treatment is operated in Zn（NO3）2 aqueous solutions. 相似文献
5.
为了深入探究岩石物理力学性质,选取红砂岩作为试验材料,以冻融循环次数、围压作为研究指标,通过设计影响因素测试试验,探究这两项指标对岩石性能的影响。试验测试结果表明,围压、冻融循环次数两项影响因素对岩石的三轴抗压强度、弹性模量均有较大影响,力学性能变化显著。 相似文献
6.
为了研究补偿收缩混凝土的抗冻性能,采用慢冻法对普通混凝土和补偿收缩混凝土进行冻融对比试验。通过对比研究普通混凝土和补偿收缩混凝土冻融后质量损失、强度损失和相对动弹性模量变化趋势,从而得出补偿收缩混凝土的抗冻性能。试验结果表明,普通混凝土冻融100次后,质量损失率为2.09%,抗压强度下降35.2%,相对动弹性模量下降到60.8%;补偿收缩混凝土质量损失率为1.62%,抗压强度下降30.3%,相对动弹性模量下降到64.8%;试验三个参数指标表明添加膨胀剂有助于提高混凝土抵抗冻融破坏的能力,改善混凝土结构的损伤程度,体现了膨胀剂对混凝土的增强机理。 相似文献
1